Press and Sinter

Using powder raw materials produced in-house, AmeriTi Parts is able to produce net shape titanium parts in nearly any alloy combination.  Currently, AmeriTi is producing parts using the following alloys:

 

 

Commercially pure titanium (CP-4)

3% Aluminum - 2.5% Vanadium (Ti3Al2.5V)

6% Aluminum - 4% Vanadium (Ti6Al4V)

The alloys mentioned above have properties after pressing that are very close to the properties achieved by traditional machined titanium parts.  Listed below are some typical mechanical properties achieved by AmeriTi:

Material                         UTS (KSI)                         YS (KSI)                         %E

Ti CP-4                              74                                     57                               12

Ti CP-4 HIP                       87                                     73                               12

Ti 3Al2.5V                         98                                     85                                7

Ti 6Al4V                            105                                   90                                6

Ti 6Al4V HIP                     120                                   110                             10

In addition, the properties attained by titanium press and sinter compare very favorably with press and sinter parts using other metals.  

Material                                   Density g/cc                         UTS (Psi 000's)

Ti CP-4                                             4.0                                            74

Ti 6Al4V                                           3.8                                           105

304 SS                                             6.4                                            43

316 SS                                             6.8                                            41

F - 240S (Steel)                               7.0                                            38

201 AB (Aluminum)                       2.8                                            20

CT 1000 (Copper Bronze)             8.0                                            30

The metallography of CP-4 both before and after a HIP cycle can be seen below.  You can see that the porosity is cured during the HIP cycle.

Before HIP 90% Density (74 KSI)

After HIP 98% Density (87 KSI)